1 2 in.
Bending 6061 aluminum sheet.
O 0 0 0 1t 1t 1t 1 1 2 t 2t.
Aluminum minimum bend radii for 90 degree cold forming of sheet and plate.
1 16 in.
Recommended minimum bend radii for 90 degree cold forming of sheet plate temper 1 64 in.
This site should not be used to determine if a.
Since commercial sheet metal bending can be done with less concern for stresses caused during forming operation the radius can be near zero for thin sheet metal.
What about the 6061t6 aluminum plate bending 90 degrees compared to the 3000 series and 5000 series.
Steel american iron and steel institute 1 see aisi s fabrication guidlines for cold bending thk 6061 t6.
To our valued customers.
That is it gets stronger and harder by working bending it.
The data provided on our website has been vetted to the best of our availabilities.
Aluminum where necessary 5052 h32 may be bent to 1t and 6061 t6 to 1 1 2t.
The 6061 t6 aluminum sheet has stable performance and high hardness is widely used in industry such as trucks buildings ships vehicles furniture machinery moulds etc.
3 8 in.
Per the aluminum association inc.
This is generalizing as there are ways to bend 6061 but for general bending you use 3003 or 5052 grain direction bend line should go across the grain for the best bend having said that a typical sharp 90 bend on a piece of 1 8 aluminum sheet should be a minimum 1 8 inside radius use either 3003 or 5052 ideally the bend line should go.
1 32 in.
1 8 in.
But the question remains the same which alloy is the best product for bending.
In my 40 plus years in the trade i have bent quite a lot of 6061 t6 aluminum.
When you are bending 0 25 in thick 6061 t6 cracking can occur when bending past an external angle of just 86 degrees.
Chances are that you ll never make it to 90 degrees much less make it to an external angle of 100 degrees.
The bend radii listed are standard minimum if manufacturing for aircraft and aerospace applications.
1 4 in.
The minimum bend radius data shown in these charts is measured to the inside of the bend.
Just like all sheet metal aluminum work hardens during the forming process.
From non heat treatable 3003 and 5052 to the heat treatable 2024 6061 and 7075 you have many options from which to choose.
Will 6061t6 aluminum plate will be cracked at 90 degrees.
3 16 in.